Morphological Evolution of Single-Core Multi-Strand Wires during Ultrasonic Metal Welding

Abstract

Ultrasonic metal welding (USMW) finds widespread utilization in automotive industries, where it is used for connecting the wire harness of the vehicle, consisting of stranded wires, to the terminals. However, the behavior of the strands during the compaction process is still understudied and often overlooked. Therefore, this work focuses on the investigation of the wire compaction behavior from a morphological point of view. A newly developed method for investigating cross-sections of such joints is introduced, facilitating area quantification of the strands for a microscale examination of compaction variations for every single strand as a function of welding time. It is shown that the deformation in the wire is not homogenous throughout the wire cross-section; instead, the formation of distinct zones is observed. Three distinct regimes dominating the welding process were observed: (i) linear reduction in nugget height with primary compaction of the nugget and sealing of the interstitial spaces between the strands for weld times from 0 s up to 1.3 s; (ii) accelerated loss of nugget height due to strong plastic deformation of the strands for weld times between 1.3 s and 1.7 s; and (iii) comprehensive welding of the individual strands and strong loss of nugget height. Furthermore, it was demonstrated that the deformation of the wire during the USMW process originates in the coupling area of the horn and the wire and not in the interface of the wire and the terminal. Therefore, it can be assumed that the temperature of the interface between the horn and the wire must be significantly higher than that of the interface between the wire and the terminal. The presented approach and new insights into the behavior of ultrasonically welded joints of stranded wires and terminals provide guidance for improving the welding process.

Keywords

• ultrasonic metal welding
• light microscopy
• aluminum
• copper
• morphology