Effect of Semi-Aging Heat Treatment on Microstructure and Mechanical Properties of an Inertia Friction Welded Joint of FGH96 Powder Metallurgy Superalloy

Abstract

Inertia friction welded joints often present different microstructures than the base metal, and subsequent heat treatment processes are always needed to maintain superior performance. This study investigates the effect of semi-aging heat treatment after welding on the microstructure, residual stress, micro-hardness, and tensile properties of inertia friction welded FGH96 powder metallurgy superalloy using optical microscopy, scanning electron microscopy, X-ray diffraction, and hardness and tensile tests. The results show that the semi-aging heat treatment after welding does not affect the grain size or grain morphology of the base metal. However, the recrystallization process can be further promoted in the weld nugget zone and transition zone. Meanwhile, the grain size is refined and the residual stress is significantly reduced in the welded joint after the same heat treatment. Under the synergetic strengthening effect of the γ′ phase, semi-aging heat treatment increased the micro-hardness of the weld nugget zone from 470 HV to 530 HV and improved the average tensile strength at room temperature by 118 MPa. These findings provide a reference for the selection of the heat treatment process after inertia friction welding of nickel-based powder metallurgy superalloys.

Keywords

• FGH96
• inertia friction welding
• aging heat treatment
• recrystallization
• mechanical properties