Effect of Pre-Fatigue on the Monotonic Deformation Behavior of a Coplanar Double-Slip-Oriented Cu Single Crystal

Abstract

The [ 2 ¯ 33 ] coplanar double-slip-oriented Cu single crystals were pre-fatigued up to a saturation stage and then uniaxially tensioned or compressed to fracture. The results show that for the specimen pre-fatigued at a plastic strain amplitude γpl of 9.2 × 10−4, which is located within the quasi-plateau of the cyclic stress-strain (CSS) curve, its tensile strength and elongation are coincidently improved, showing an obvious strengthening effect by low-cycle fatigue (LCF) training. However, for the crystal specimens pre-fatigued at a γpl lower or higher than the quasi-plateau region, due to a low pre-cyclic hardening or the pre-induction of fatigue damage, no marked strengthening effect by LCF training occurs, and even a weakening effect by LCF damage takes place instead. In contrast, the effect of pre-fatigue deformation on the uniaxial compressive behavior is not so significant, since the compressive deformation is in a stress state more beneficial to the ongoing plastic deformation and it is insensitive to the damage induced by pre-cycling. Based on the observations and comparisons of deformation features and dislocation structures in the uniaxially deformed [ 2 ¯ 33 ] crystal specimens which have been pre-fatigued at different γpl, the micro-mechanisms for the effect of pre-fatigue on the static mechanical behavior are discussed.

Keywords

• Cu single crystal
• coplanar double slip
• pre-fatigue deformation
• plastic strain amplitude
• tensile behavior
• compressive behavior
• dislocation structure