Comparison of Two Intergranular Corrosion Tests on EN AW-6016 Sheet Material

Abstract

Two different intergranular corrosion tests were performed on EN AW-6016 sheet material, an ISO 11846:1995-based test with varying solution amounts and acid concentrations, and a standard test of an automotive company (PV1113, VW-Audi). The average intergranular corrosion depth was determined via optical microscopy. The differences in the intergranular corrosion depths were then discussed with regard to the applicability and quality of the two different test methods. The influence of varying test parameters for ISO 11846:1995 was discussed as well. The determined IGC depths were found to be strongly dependent on the testing parameters, which will therefore have a pronounced influence on the determined IGC susceptibility of a material. In general, ISO 11846:1995 tests resulted in a significantly lower corrosion speed, and the corrosive attack was found to be primarily along grain boundaries.

Keywords

• intergranular corrosion
• Al-Mg-Si wrought alloys
• (standardized test norms) corrosion test