Hydrochloric Acid Leaching Behaviors of Copper and Antimony in Speiss Obtained from Top Submerged Lance Furnace

Abstract

Copper (Cu) has been recovered from speiss generated from top submerged lance furnace process, but it was reported that the leaching efficiency of Cu in sulfuric acid solution decreased with increasing antimony (Sb) content in the speiss. Scanning electron microscopy (SEM)–energy-dispersive X-ray spectroscopy (EDS) results indicate that Sb exists as CuSb alloy, which would retard the leaching of Cu. Therefore, hydrochloric acid leaching with aeration was performed to investigate the leaching behaviors of copper and antimony. The leaching efficiency of Cu increased with increasing agitation speed, temperature, HCl concentration, and the introduction ratio of O2, but also with decreasing pulp density. The leaching efficiency of Cu increased to more than 99% within 60 min in 1 mol/L HCl solution at 600 rpm and 90 °C with 10 g/L pulp density and 1000 cc/min O2. The leaching efficiency of Sb increased and then decreased in all 1 mol/L HCl leaching tests, and precipitate was observed in the leach solution, which was determined to be SbOCl or Sb2O3 by XRD analyses. However, in 2 mol/L–5 mol/L HCl solutions, the leaching efficiency of Sb increased to more than 95% (about 900 mg/L) and remained, so more than 2 mol/L HCl could stabilize Sb ion in the HCl solution.

Keywords

• copper
• antimony
• hydrochloric acid leaching
• speiss