The effect of 60Co gamma irradiation on coal fly-ash geopolymer paste setting time

Abstract

Cementation is the baseline technology for conditioning of low to intermediate level radioactive waste. Geopolymers, a class of alkali activated binders, are a promising new material for radioactive waste treatment. Coal fly-ash based geopolymers are a low-cost, low greenhouse gas footprint alternative to metakaolin based materials. Both the grouting of sludge/powders/liquids and encapsulation of solids/compacted waste rely on the grout maintaining optimal flow (rheological properties) during the mixing and pouring operations, and achieving a set leading to proper long term solidification (mechanical properties). The initial and final setting time for fly-ash geopolymer paste, based on the SRPS EN 196-3 standard, has been measured upon irradiation by gamma rays in a 60Co reference field positioned with a kerma air rate of 3.42 mGys–1. The binder paste was prepared using fly-ash from the TENT B power plant's electrostatic filters without further sieving, activated by water glass with module 1.5 and mixed with distilled water until a satisfactory flow was obtained, and poured into the sample and control molds. The initial and final setting times for the irradiated sample and non-irradiated control were determined by the Vicat apparatus. The irradiated sample demonstrated an 11 % shorter initial setting time, and 16 % shorter final setting time, compared to the control.

Keywords

• geopolymer
• setting time
• gamma irradiation
• alkali-activated binder