Thermal Evolutions to Glass-Ceramics Bearing Calcium Tungstate Crystals in Borate Glasses Doped with Photoluminescent Eu³⁺ Ions

Abstract

Thermal evolutions of calcium-tungstate-borate glasses were investigated for the development of luminescent glass-ceramics by using Eu3+ dopant in a borate glass matrix with calcium tungstate, which was expected to have a combined character of glass and ceramics. This study revealed that single-phase precipitation of CaWO4 crystals in borate glass matrix was possible by heat-treatment at a temperature higher than glass transition temperature Tg for (100−x) (33CaO-67B2O3)−xCa3WO6 (x = 8−15 mol%). Additionally, the crystallization of CaWO4 was found by Raman spectroscopy due to the formation of W=O double bondings of WO4 tetrahedra in the pristine glass despite starting with the higher calcium content of Ca3WO6. Eu3+ ions were excluded from the CaWO4 crystals and positioned in the borate glass phase as a stable site for them, which provided local environments in higher symmetry around Eu3+ ions.

Keywords

• glass-ceramics
• calcium tungstates
• borate glasses
• Eu³⁺ luminescence
• asymmetry ratio