Effect of Water Magnetization Technique on the Properties of Metakaolin-Based Sustainable Concrete

Abstract

Using metakaolin (MK) in concrete with magnetized water (MW) has a high possibility to enhance concrete suitability. In this study, the effect of using MK and MW on concrete characteristics was studied through testing twelve concrete mixes. Seven ratios of MK were used in this study, namely 0%, 5%, 10%, and 20%, as an alternative to cement and +5%, +10%, and +20% as a cement additive. In addition, five water magnetization methods were applied on MK concrete. In the first stage of this study, the impact of different MK ratios on the workability of concrete, compressive strength, flexural strength, and tensile strength was studied using traditional tap water (TW) as the concrete mixing water. In the second stage, the best mix (best MK ratio) from the first stage was chosen to study the effect of the water magnetization method on concrete properties and to determine the best method for water magnetization. Scanning electronic microscope (SEM) analysis was also carried out on selected mixes to closely investigate the effect of MK and MW on concrete microstructure. The results showed that the best ratio of MK in concrete was +10% (MK as a 10% cement addition), and the best water magnetization method was to pass the water through 1.6 tesla then through 1.4 tesla magnetic fields. The SEM analysis confirmed the absence of pores after using MW instead of regular TW by increasing the calcium silicate hydrate (CSH) gel and reducing calcium hydroxide (CH). Using MK and MW enhanced the compressive strength by up to 33%, 32%, and 27% at 7, 28, and 365 days, respectively, and MW enhanced the workability by up to 3% compared to that of the control mix.

Keywords

• magnetized water
• metakaolin
• SEM analysis
• compressive strength
• workability