Design, Manufacturing, Microstructure, and Surface Properties of Brazed Co-Based Composite Coatings Reinforced with Tungsten Carbide Particles

Abstract

Brazing is a joining process that involves melting a filler metal and flowing it into the joint between two closely fitting parts. While brazing is primarily used for joining metals, it can also be adapted for certain coating deposition applications. The present study investigates the microstructure and corrosion behavior and sliding wear resistance of WC (Tungsten Carbide)-CoCr-Ni reinforced Co-based composite coatings deposited onto the surface of AISI 904L stainless steel using a vacuum brazing method. The primary objective of this experimental work was to evaluate the influence of WC-based particles added to the microstructure and the properties of the brazed Co composite coating. The focus was on enhancing the sliding wear resistance of the coatings while ensuring that their corrosion resistance in chloride media was not adversely affected. The morphology and microstructure of the composite coatings were investigated using scanning electron microscopy (SEM) and phase identification by X-ray diffraction (XRD). The SEM analysis revealed in the coating the presence of intermetallic compounds and carbides, which increase the hardness of the material. The sliding wear resistance was assessed using the pin-on-disk method, and the corrosion properties were determined using electrochemical measurements. The results obtained showed that as the WC particle ratio in the Co-based composite coating increased, the mechanical properties improved, the alloy became harder, and the tribological properties were improved. The evaluation of the electrochemical tests revealed no significant alterations of the manufactured composite in comparison with the Co-based alloys. In all cases, the corrosion behavior was better compared with that of the stainless-steel substrate.

Keywords

• co-based coatings
• brazing
• wear resistance
• corrosion behavior