High Temperature Fatigue Behavior and Failure Mechanism of Ti-45Al-4Nb-1Mo-0.15B Alloy

Abstract

Strain-controlled low cycle fatigue experiments were carried out on the TiAl alloy Ti-45Al-4Nb-1Mo-0.15B at 400 °C and 750 °C to reveal the cyclic mechanical behavior and failure mechanism. The TiAl alloy presents stable cyclic characteristics under fatigue loading at elevated temperatures. No obvious cyclic softening or cyclic hardening was manifested during experiments. The cyclic stress–strain relationship is well described by the Ramberg–Osgood equation. The fatigue lifetime at different temperatures has a log-linear relationship with the total strain ranges. The fracture morphology indicates the main fracture mode of fatigue specimens at 400 °C is a brittle fracture, while there is a ductile fracture at 750 °C. Meanwhile, the trans-lamellar fracture is dominant for the lamellar microstructure and the percentages of the inter-lamellar fracture decreases with the strain amplitude.

Keywords

• TiAl alloy
• strain-controlled fatigue behavior
• cyclic stress–strain relationship
• failure mechanism
• fracture morphology