The effect of laser irradiation on electrical and structural properties of ZnO thin films

Abstract

In this paper, ZnO thin film was prepared by sol-gel process on glass substrates. The deposited films were dried at 100 and 240 ˚C and then annealed at 300, 400 and 500 ˚C. The two-probe measurement showed that resistance of as-prepared films is very high. The KrF excimer (λ=248 nm) laser irradiation with 1000 pulses, frequency of 1 Hz and 90 mJ/cm2 energy on surface of film resulted in the reduction of the films electrical resistance. X-ray diffraction (XRD) patterns confirmed the improved hexagonal wurtzite structure of film, and AFM and FE-SEM analyses showed regular and spherical grain was formed on the surface. The particle size was increased from ~10 to ~30 nm after leaser irradiation. Generally, it was showed that electrical, structural and morphological properties of films improve considerably by laser irradiation.

Keywords

• ZnO thin films
• transparent conductor oxide
• pulsed laser
• XRD
• AFM