Coating based on basalt protection metal structures

Abstract

The paper present the results of the synthesis of a new refractory coating based on basalt for the protection of metal construction under conditions of cavitation. Initial basalt samples obtained from the locality Vrelo - Kopaonik. The basalt based refractory filler was obtained by crushing and grinding selected samples of basalt rock. XRD, SEM and optical microscopy methods were used to characterize the obtained filler samples. The research defined the composition of basalt -based coating with epoxy resinbased binder, organic additives and organic solvent. The resistance properties of protective coatings applied to metal surface were investigated using the ultrasonic vibration method with a stationary sample according to the ASTM G 32 standard. To evaluate the resistance of the sample surface to the action of cavitation, the sample surface was examined before and during testing. The surface of the samples was monitored by scanning electron microscopy in order to analyze the morphology of surface damage. Computer image analysis according to the Image Pro Plus program was applied to assess the damage to the sample surface. The obtained test results showed high resistance of the coating layers to the effect of cavitation, with small mass losses, small damage to the coating surface and a cavitation rate of 0,1 mg/min.

Keywords

• basalt
• protective coating
• cavitation resistance
• mass loss