Highly-Densified Panels from Hyun Aspen (Populus alba × glandulosa) Wood with Different Delignification Levels Using Alkaline Hydrogen Peroxide Pretreatment

Abstract

Defect-free, highly-densified panels without springback were prepared from Hyun aspen (Populus alba × glandulosa) wood with different delignification levels by alkaline hydrogen peroxide (AHP) pretreatment. The AHP concentrations were adjusted to 3%, 7%, 10%, while the temperature (100 °C), time (3 h), pH (11), liquor ratio (6.25), and stabilizer (0.5% EDTA) remained constant. The delignification of Hyun aspen wood panels was indirectly quantified by analyzing the UV absorbance of the spent liquor after AHP treatment, wherein delignification ranged from 12% to 58% depending on the AHP concentration. To achieve highly-densified panels, the densification conditions, such as pressure, temperature, and time, were examined. Panels subjected to cold-pressing (25 °C) at 30 MPa for 1 h, followed by hot-pressing (105 °C) at 30 MPa for 6 h, then immediately removed after heating, resulted in durable, highly-densified panels with no springback or cracks.

Keywords

• hyun aspen
• alkaline hydrogen peroxide
• delignification
• densification
• panel