Effects of Ultrafine Fly Ash against Sulphate Reaction in Concrete Structures

Abstract

In this study, Afşin Elbistan C-type fly ash (FA) was used, which protects against the sulphate reaction that damages concrete. The detrimental effects of post-reaction decrease with increasing fly ash fineness. The study used 10%, 30%, and 50% weight substitutes of cement. The fly ash was ground in a ball mill for 0, 10, 20, 30, 45, and 60 min, and Blaine fineness values of 1555, 1632, 2347, 2589, 2766, and 3433 cm2/g were obtained, respectively. The effect of the samples on the sulphate resistance was investigated by exposing the samples to 5% or 10% added sulphate solutions, and the compressive strength and ultrasonic pulse velocity of the concrete were tested. The compressive strength values obtained decreased with the increase in sulphate content, and the increase in the grinding time and the amount of substituted FA increased the compressive strength values. It was observed that weight loss increased with increasing sulphate content and decreased with the addition of FA with a high Blaine fineness. It was determined that as the Blaine fineness value increased, the sulphate content, FA substitution amount, and ultrasonic pulse speed decreased. This study was carried out to determine the effects of fly ash used at different fineness and replacement ratios on the performance and strength of concrete after exposure to external influences such as sulphate. The use of fly ash instead of cement will reduce the use of waste materials and natural resources and prevent environmental pollution. The cost of cement and concrete will be reduced.

Keywords

• Blaine fineness
• waste fly ash
• cement
• concrete
• substitution rate
• sulphate composition