Carbones activos con propiedades de tamiz molecular

Abstract

Carbon molecular sieves with micropore diameters of 0.41-0.54 nm were obtained by activation with water vapour to 6% burnoff of chars from oxidized bituminous coals and semianthracite. A temperature of 750ºC and a flow rate of 100 mL.min-1 of N2 with a 12.4% of steam content were used. Less developed microporosity was obtained from anthracite, that needed a 12% burn-off in order to obtain similar micropore development and size distribution. Activation temperature has an important influence in the development of microporosity of chars from anthracite. For chars from low rank coals narrower micropore size distributions can be obtained by using in the activation a low stream flow rate.<br><br>Se prepararon tamices moleculares de carbono con distribución de microporos preferente en el intervalo 0,41-0,54 nm por activación al 6% de carbones bituminosos y de semiantracita preoxidados, a 750ºC y bajo flujos de 100 mL.min-1 de N2 con un contenido del 12,4% de vapor de agua; a partir de antracita activada se obtuvo un menor desarrollo microporoso, necesitando un grado de quemado del 12% para lograr distribuciones y desarrollos microporosos similares. La temperatura de activación ejerce una influencia importante en el desarrollo microporoso de la antracita, que es mayor si la temperatura utilizada durante el proceso es mas alta. El uso de flujos bajos de N2/vapor de agua durante la activación de los carbones bituminosos conduce a carbones activados con distribuciones de la anchura de microporos más estrechas.

Keywords

• Carbon molecular sieve
• active carbon
• immersion calorimetry
• Tamiz molecular de carbono
• carbón activo
• calorimetría de inmersión