Optical and Electrochemical Characterization of Nanoporous Alumina Structures: Pore Size, Porosity, and Structure Effect

Abstract

Three nanoporous alumina structures (NPASs) obtained by the two-step anodization method were optically and electrochemically characterized. Two of the structures were symmetric (NPAS-Sf and NPAS-Ph) and one was asymmetric (NPAS-And); pore size ranged from 10 nm to 100 nm and porosity was 12% in the case of the symmetrical NPAS and 23% and 30% for each surface of the asymmetric structure NPAS-And(A) and (B), respectively. Optical parameters of the studied samples (refraction index and extinction coefficient) were obtained from ellypsometric spectroscopy measurements carried out for wavelengths ranging between 250 nm and 1700 nm (visible and near infrared regions), with the total average refraction indices being 1.54, 1.52, 1.14, and 1.05 for NPAS-Sf, NPAS-Ph, NPAS-And(A), and NPAS-And(B), respectively, which indicates porosity control of refraction index values. Electrochemical characterizations (concentration potential and impedance spectroscopy measurements) were performed with NaCl solutions, and they allowed us to estimate samples of effective fixed charge concentration (1.22 × 10−2 M, 1.13 × 10−3 M, and 1.15 × 10−3 M), ion transport numbers, permselectivity (33.0%, 3.1%, and 9.6%), and the electrical resistance of each solution/sample system as well as the interfacial effects associated to solution concentration–polarization, which seems to be mainly controlled by pore size and sample symmetry.

Keywords

• nanoporous alumina structures
• ellypsometric spectroscopy
• concentration potential
• impedance spectroscopy
• sample structure