This paper demonstrates the successful printing of H13 tool steel by a selective laser melting (SLM) method at a scan laser speed of 200 mm/s for the best microstructure and mechanical behavior. Specifically, the nanoindentation strain-rate sensitivity values were 0.022, 0.019, 0.027, 0.028, and 0.035 for SLM H13 at laser scan speeds of 100, 200, 400, 800, and 1600 mm/s, respectively. This showed that the hardness increases as the strain rate increases and, practically, the hardness values of the SLM H13 at the 200 mm/s laser scan speed are the highest and least sensitive to the strain rate as compared to H13 samples at other scan speeds. The SLM processing of this material at 200 mm/s laser scan speed therefore shows the highest potential for advanced tool design. Residual stress is expected to affect the hardness and shall be investigated in future research.