Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2005)

Efectos de la microestructura en las propiedades magnéticas de imanes híbridos de SrFe<sub>12</sub>O<sub>19</sub>/MQP-Q

  • Ayala Valenzuela, O.,
  • Coral Flores, V.,
  • Matutes Aquino, J. A.,
  • Bueno Baqués, D.

Journal volume & issue
Vol. 44, no. 4
pp. 228 – 230

Abstract

Read online

Magnetic properties in Hybrid magnets, compression-molded consisting on mixtures of SrFe12O19 ferrite and MQP-Q (Nd2Fe14B + αFe) embedded in LLDPE were studied. Samples with the ratio %wt ferrite/%wt MQP-Q 4/82, 48/6 and 26/68 are compared to powders of pure starting magnetic materials. Microstructure was investigated by SEM and EDS. Magnetic interactions have been studied by isothermal remanence (IRM), dc-demagnetization remanence (DCD) curves. Hybrid samples show interactions initially positive, falling rapidly through zero, with a negative minimum, as the magnetic field increases. The effect of the microstructure in the ΔM curves is discussed.En este trabajo se estudiaron la microestructura y propiedades magnéticas de imanes híbridos moldeados por compresión, constituidos por mezclas de Ferrita de Estroncio (SrFe12O19) y MQP-Q (Nd2Fe14B + αFe) embebidas en una matriz de Polietileno Lineal de Baja Densidad (LLDPE). Se comparan las propiedades de las muestras con una relación % en peso de ferrita / % en peso de MQP-Q de 4/82, 48/6 y 26/68 con polvos de los materiales de partida. La microestructura se estudió por microscopía electrónica de barrido y microanálisis elemental. Las interacciones magnéticas fueron estudiadas por medio de curvas de desmagnetización isotérmica (IRM) y de desmagnetización DC (DCD). Se observan interacciones inicialmente positivas, que decrecen pasando por cero, con un mínimo negativo, a medida que se incrementa el campo magnético. Se discute el efecto de la microestructura en las curvas de ΔM.

Keywords