Microstructural Investigation of Process Parameters Dedicated to Laser Powder Bed Fusion of AlSi7Mg0.6 Alloy

Abstract

This study presents a microstructural investigation of the printing parameters of an AlSi7Mg0.6 alloy produced by powder bed fusion (PBF) using laser beam melting (LB/M) technology. The investigation focused on the effects of laser power, exposure velocity, and hatching distance on the microhardness, porosity, and microstructure of the produced alloy. The microstructure was characterized in the plane of printing on a confocal microscope. The results showed that the printing parameters significantly affected the microstructure, whereas the energy density had a major effect. Decreasing the laser power and decreasing the hatching distance resulted in increased porosity and the increased participation of non-melted particles. A mathematical model was created to determine the porosity of a 3D-printed material based on three printing parameters. Microhardness was not affected by the printing parameters. The statistical model created based on the porosity investigation allowed for the illustration of the technological window and showed certain ranges of parameter values at which the porosity of the produced samples was at a possible low level.

Keywords

• additive manufacturing
• metallography
• porosity
• microhardness
• AlSi7Mg0.6