Influence of Pre- and Post-Contouring Strategies to Downskin Sloped Surfaces in Laser Powder-Bed Fusion (L-PBF) Additive Manufacturing

Abstract

Among various metal additive manufacturing (AM) technologies, L-PBF is known for fabricating intricate components. However, due to step edges and powder particle attachments, attaining a good surface finish is challenging, especially on downskin surfaces. Contour scanning has potential to improve surface quality because such scanning may dominate the surface formation of sloped features. This study evaluates the effects of pre- and post-contouring strategies on the sloped downskin surfaces fabricated using a commercial L-PBF system with Ti6Al4V powder. L-PBF parts printed at inclination angles 30°, 45° and 60° were investigated. A double-contouring approach with varying processing conditions was employed and surface characteristics were analyzed using data acquired by white light interferometry. The average surface roughness, Sa, surface skewness, Ssk, and percentage area of powder particles attached onto surfaces were statistically evaluated. The lowest Sa obtained for pre- and post-contoured samples is 14.08 µm and 18.88 µm, respectively. For both strategies, the combination of a low laser power and a high scan speed on the interface of downskin surface and underneath powder results in smoother surfaces. However, while comparing both strategies, pre-contouring gives better surface finish for samples built at similar processing conditions, with a difference of nearly 5 µm in Sa.

Keywords

• downskin surfaces
• surface roughness
• laser powder-bed fusion
• contouring strategies