تحقیقات علوم چوب و کاغذ ایران (Dec 1998)
Investigating on the possibility of making particleboard from lignocellulosic sources on southern of Iran (Potential for using wood tamarix in particleboard industries).
Abstract
The physical and mechanical properties were determined of particleboards produced from Tamarix wood using 3 resin contents (9, 10 and 11%) and 3 pressing times (5, 6 and 7 min). Other factors such as resin type, hardener type, closing press time, mat moisture and board density (etc.) were assumed invariable. Three boards were. produced for each combination of the 2 variable types. Based on DIN-68763 standard physical and mechanical properties including modulus of rupture (MOR), modulus of elasticity (MOE), internal bond (IB) strength and thickness swelling after 2 and 24 h immersion in water (TS2 and TS24) were tested. The best results were obtained with 11% resin and 6 min pressing time.