Surface roughness and chemical composition changes of resin-modified glass ionomer immersed in 0.2% sodium fluoride solution

Abstract

Background/purpose: Glass ionomers undergo degradation when exposed to fluoride, which changes the physico-chemical characteristics of the materials. The purpose of this study was to evaluate the surface changes of resin-modified glass ionomer (RMGI) when immersed in a sodium fluoride (NaF) solution according to pH and time. Materials and methods: 120 RMGI specimens were prepared, and 30 specimens were placed in four types of storage solutions for four weeks; pH 7 artificial saliva with or without 0.2% NaF (As7 and NaF7), pH 5 artificial saliva with or without 0.2% NaF (As5 and NaF5). Interferometry and microscopy were performed to evaluate the surface roughness and topography, while spectroscopy was used to analyze the chemical composition changes. Results: Rougher topography and increased roughness was exhibited in NaF groups, owing to the disintegration of the polysalt matrix. Reduced Sr and F was exhibited in all groups, whereas NaF group showed a decrease in Al and inorganic components. Conclusion: This study suggest that excessive use of fluoride therapy could lead to severe degradation of RMGI.

Keywords

• Chemical composition
• Fluoride
• RMGI
• Surface degradation
• Surface roughness