Optimization of Photogenerated Charge Carrier Lifetimes in ALD Grown TiO₂ for Photonic Applications

Abstract

Titanium dioxide (TiO2) thin films are widely employed for photocatalytic and photovoltaic applications where the long lifetime of charge carriers is a paramount requirement for the device efficiency. To ensure the long lifetime, a high temperature treatment is used which restricts the applicability of TiO2 in devices incorporating organic or polymer components. In this study, we exploited low temperature (100–150 °C) atomic layer deposition (ALD) of 30 nm TiO2 thin films from tetrakis(dimethylamido)titanium. The deposition was followed by a heat treatment in air to find the minimum temperature requirements for the film fabrication without compromising the carrier lifetime. Femto-to nanosecond transient absorption spectroscopy was used to determine the lifetimes, and grazing incidence X-ray diffraction was employed for structural analysis. The optimal result was obtained for the TiO2 thin films grown at 150 °C and heat-treated at as low as 300 °C. The deposited thin films were amorphous and crystallized into anatase phase upon heat treatment at 300–500 °C. The average carrier lifetime for amorphous TiO2 is few picoseconds but increases to >400 ps upon crystallization at 500 °C. The samples deposited at 100 °C were also crystallized as anatase but the carrier lifetime was <100 ps.

Keywords

• titanium dioxide
• atomic layer deposition
• transient absorption spectroscopy
• thin films
• lifetime of charge carriers