Photocatalytic Performance of Functionalized Biopolymer for Neodymium (III) Sorption and the Recovery from Leachate Solution
Abstract
Successive grafting of new sorbent bearing amino phosphonic groups based on chitosan nano magnetite particles was performed through successive coupling with formaldehyde. The produced composite was characterized by the high sorption capacity toward rare earth elements (REEs) and consists of different types of functional groups (phosphonic, hydroxyls and amine groups) that are used for enhancing the sorption properties. The chemical modification and the sorption mechanism were investigated through different analytical tools; i.e., FTIR, SEM, SEM-EDX, TGA, BET (surface area) and pHpzc. The sorption was investigated toward Nd(III) as one of the REE(III) members under ultraviolet (UV) and visible light (VL) conditions. The optimum sorption was found at pH0 4 and the sorption capacity was recorded at 0.871 and 0.779 mmol Nd g−1 under UV and VL respectively. Sorption isotherms and uptake kinetics were fitted by Langmuir and Sips and by pseudo-first order rate equation (PFORE) for the functionalized sorbent, respectively. The sorbent showed a relatively high-speed sorption kinetic (20 min). The bounded metal ions were progressively eluted using 0.2 M HCl solution with a desorption rate 10–15 min, while the loss in the total capacity after a series of sorption recycling (sorption/desorption) (five cycles) was limited (around 3%) with 100% of the desorption efficiency, indicating the high stability of the sorbent toward an acidic medium. The sorbent was used for the recovery of REEs from leach liquor residue after pretreatment for the extraction of particular elements. From these results (high loading capacity, high selectivity and high stability against acid treatments), we can see that the sorbent is a promising tool for the selective recovery of rare earth elements in the field of metal valorization.
Keywords