Synthesis and Thermal Properties of Cerium-Dysprosium Oxide

Abstract

The paper presents results of investigation on synthesis and characterization of cerium-dysprosium oxide. The input powders - dysprosium oxide Dy2O3 and cerium oxide CeO2 - were mixed so as to obtain equimolar ratio of cations, milled in alcohol and synthesized via solid state reaction process at 1350°C under 15MPa in vacuum for 2h. The microstructure, phase composition and thermal properties were analyzed. The obtained material was multiphase. Non-stoichiometric compounds were identified. Thermal diffusivity of investigated material decreased in the temperature range of 25-1000°C from 0,71 to 0,45 mm2/s.

Keywords

• cerium oxide
• dysprosium oxide
• thermal properties
• TBC