Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 2006)
Comportamiento en fractura de un eutéctico Al<sub>2</sub>O<sub>3</sub>/YAG crecido por solidificación direccional
Abstract
This investigation was aimed to analyse the mechanical behaviour of an eutectic ceramic Al2O3/YAG processed by directional solidification in a Bridgman furnace. Fracture toughness and young modulus were measured through three point bend tests from room temperature up to 1650 ºC. These tests were performed under stroke control using two different cross-head speeds to analyse the influence of strain rate on the fracture behaviour. The material was brittle up to 1400 ºC and plastic deformation was found at higher temperature. Plastic deformation was reduced, or even disappeared, when the strain rate was increased. Finally, the investigation was completed with the analysis of the deformation and fracture micromechanisms in the crack tip.Esta investigación se ha centrado en el estudio de un eutéctico cerámico Al2O3/YAG fabricado por solidificación direccional mediante el método de Bridgman. Se han realizado ensayos de tenacidad de fractura por flexión en tres puntos y se ha medido el módulo de elasticidad entre temperatura ambiente y 1650 ºC. Así mismo se han utilizado dos velocidades de ensayo para analizar la influencia de la velocidad de deformación en el comportamiento en fractura. El comportamiento ha sido frágil hasta 1400 ºC, temperatura a partir de la cual comienzan a aparecer fenómenos plásticos. Estos se reducen o desaparecen cuando se aumenta la velocidad de deformación del material. Finalmente, el estudio se ha completado con el análisis de los mecanismos de deformación y rotura en el frente de la grieta.