Conferring NiTi alloy with controllable antibacterial activity and enhanced corrosion resistance by exploiting Ag@PDA films as a platform through a one-pot construction route

Abstract

The lack of antibacterial activity and the leaching of Ni ions seriously limit the potential applications of the near equiatomic nickel-titanium (NiTi) alloy in the biomedical field. In this study, a silver nanoparticles (Ag NPs) wrapped in a polydopamine (Ag@PDA) film modified NiTi alloy with controllable antibacterial activity and enhanced corrosion resistance was achieved using a one-pot approach in a mixed solution of AgNO3 and dopamine. The controllable antibacterial activity could be achieved by adjusting the initial concentration of dopamine (Cdop), which obtained Ag@PDA films with varying thickness of polydopamine layers coated on Ag NPs, thereby conferring different levels of antibacterial activity to the modified NiTi alloy. In vitro antibacterial ratios (24 h) of Ag@PDA film-modified NiTi alloy against E.coli and S.aureus ranged from 46 % to 100 % and from 42 % to 100 %, respectively. The release curves of Ag ions indicated the persistent antibacterial effect of Ag@PDA film-modified NiTi alloy for at least 21 days. Moreover, in vitro cytotoxicity and in vivo implantation tests demonstrated the satisfactory biosafety of the Ag@PDA film-modified NiTi alloy when used as bioimplants. This research offers valuable insight into meeting various antibacterial demands for NiTi alloy implantations and highlights the potential of Ag-containing film-modified biomaterials in addressing different types of infections induced by implantations.

Keywords

• Nickel-titanium alloy
• Silver nanoparticles
• Polydopamine
• Corrosion resistance
• Antibacterial platform