Orthogonal Test Design for the Optimization of Preparation of Steel Slag-Based Carbonated Building Materials with Ultramafic Tailings as Fine Aggregates

Abstract

The high carbonation potential makes ultramafic tailings ideal aggregates for carbonated building materials. This paper investigates the preparation condition of ultramafic tailings and steel slag through orthogonal experiments. The results show that compressive strength has a positive exponential correlation with the CO2 uptake of the carbonated compacts. The optimized conditions include a slag-tailings ratio of 5:5, a carbonation time of 12 h, a grinding time of 0 min, and a water-solid ratio of 2.5:10, when the compressive strength of the carbonated compacts reaches 29 MPa and the CO2 uptake reaches 66.5 mg CO2/g. The effects on the compressive strength ordered from high to low impact are the slag/tailings ratio, carbonation time, grinding time of steel slag, and water–solid ratio. The effects on the CO2 uptake ordered from high to low impact are the slag–tailings ratio, water–solid ratio, carbonation time, and grinding time of steel slag. A high water–solid ratio hinders the early carbonation reactions, but promotes the long-term carbonation reaction. Steel slag is the main material being carbonated and contributes to the hardening of the compacts through carbonation curing at room temperature. Ultramafic tailings assist steel slag in hardening through minor carbonation and provide fibrous contents. The obtained results lay a solid foundation for the development of tailings-steel slag carbonated materials.

Keywords

• ultramafic tailings
• steel slag
• carbonation curing
• orthogonal test
• building materials