Welding of Cr-Mo cast steel with rare earth elements using the TIG welding process

Abstract

The paper shows the effect of the welding test welded joints made of TIG welding process of G17CrMo5-5 cast steel designed to operate at elevated temperatures. The test welded joints were made on two sets of melt that are unmodi ed and with rare earth metals (MZR). Modification of cast steel was performed using mischmetal cerium mixture. The authors describe the technology of welding process with the TIG method. To determine the quality of the connections carried out macroscopic observation of joints in cross-section. Hardness distribution measurements and microscopic observations of selected joint areas were performed. The authors showed differences in properties between unmodi ed and modi ed cast steel. in polish Spawanie staliwa Cr-Mo z dodatkiem pierwiastków ziem rzadkich metodą TIG W pracy przedstawiono efekty spawania złączy próbnych wykonanych metodą TIG ze staliwa G17CrMo5-5 przeznaczonego do pracy w podwyższonych temperaturach. Wykonano złącza próbne na dwóch seriach wytopów tj. niemodyfikowanego oraz z dodatkiem metali ziem rzadkich (MZR). Mody kację staliwa prowadzono przy użyciu mieszanki cerowej w postaci mischmetalu. Autorzy opisują technologię spawania złączy próbnych metodą TIG. W celu określenia jakości wykonanych połączeń przeprowadzono obserwacje makroskopowe złączy na przekroju poprzecznym. Dokonano pomiarów rozkładu twardości oraz obserwacje mikroskopowe wybranych obszarów złączy. Autorzy wykazali różnice we własnościach pomiędzy staliwem niemody kowanym a mody kowanym.

Keywords

• cast steel
• TIG welding
• hardness