Effects of Cr and Mo on Mechanical Properties of Hot-Forged Medium Carbon TRIP-Aided Bainitic Ferrite Steels

Abstract

In this study, the effects of Cr and Mo additions on mechanical properties of hot-forged medium carbon TRIP-aided bainitic ferrite (TBF) steel were investigated. If 0.5%Cr was added to the base steel with a chemical composition of 0.4%C, 1.5%Si, 1.5%Mn, 0.5%Al, and 0.05%Nb in mass%, the developed steel achieved the best combination of strength and total elongation. The best combination of strength and impact toughness was attained by multiple additions of 0.5%Cr and 0.2%Mo to the base steel. The excellent combination of strength and impact toughness substantially exceeded those of quenched and tempered JIS-SCM420 and 440 steels, although it was as high as those of 0.2%C TBF steels with 1.0%Cr and 0.2%Mo. The good impact toughness was mainly caused by uniform fine bainitic ferrite matrix structure and a large amount of metastable retained austenite.

Keywords

• hot-forging
• microalloying
• trip-aided bainitic ferrite steel
• retained austenite
• tensile property
• impact toughness