Effect of Vanadium and Titanium on Desulfurization of CaO Slag in Liquid Iron

Abstract

The possibility of vanadium and titanium participating in the CaO desulfurization reaction has been evaluated. The desulfurization products of CaO which were added to liquid iron containing vanadium−titanium in lab conditions were observed. At the early stage of adding CaO, titanium and sulfur ware agglomerated on the surface of CaO particles. The particles were composed of CaO, TiO2, and CaS. However, vanadium oxide was not detected. It was proposed that the titanium rather than the vanadium could react with CaO and sulfur. The desulfurization kinetics experiment showed that the high titanium content in liquid iron reduced desulfurization velocity, while vanadium had little effect on the desulfurization. The reason for this was that the TiO2 which surrounded the CaO particle impeded the mass transfer of sulfur. The vanadium and titanium had a little influence on the final sulfur content of CaO desulfurization. The theoretical discussion of these phenomena was carried out. The controlling reaction of final sulfur content was (CaO) + [S] + [C] = (CaS) + CO(g).

Keywords

• hot metal desulfurization
• vanadium
• titanium
• desulfurization reactions
• thermodynamics and kinetics