The Study of Hardness Evolution during the Tempering Process of 38MnB5Nb Ultra-High-Strength Hot Stamping Steel: Experimental Analysis and Constitutive Models
Abstract
To elucidate the hardness evolution behaviors for 38MnB5Nb ultra-high-strength hot stamping steel, a series of tempering processes with varying tempering temperatures and times were carried out with a dilatometer. Meanwhile, the hardness of each sample was measured after dilatometer experiments. The results indicated that the tempering process parameters (including the tempering temperature and time) play an important role in the hardness of the studied steel. The hardness of 38MnB5Nb ultra-high-strength hot stamping steel at the quenched state is about 580 Hv, while it is 240 Hv for the quasi-annealed state. As the tempering time extends, the hardness is decreased sharply at the initial stage; then, the hardness is decreased in a quasi-linear trend with a slight slope; finally, the hardness almost keeps a constant value, which depends on the tempering temperature. In addition, the tempering process has a big effect on the mechanical properties of 38MnB5Nb ultra-high-strength hot stamping steel by increasing the product of the strength and elongation by about 40%.
Keywords