Evaluation and comparing the tooth discoloration induced by cold ceramic and MTA Angelus as endodontic cements

Abstract

Background and Aims: The aim of this study was to investigate the tooth discoloration caused by cold ceramic compared to MTA Angelus in contact with the washing solutions such as sodium hypochlorite (NaOCl) and normal saline. Materials and Methods: 50 samples of extracted human maxillary anterior teeth were selected. After preparing the access cavity, they were divided into 4 experimental groups and 1 control group (10 in each group). The access cavities of teeth in groups 2 and 4 were rinsed with 5.25% sodium hypochlorite and those in groups 1 and 3 were rinsed with normal saline. Then, after drying, 3 mm thickness of cold ceramic (groups 1 and 2) and MTA Angelus (groups 3 and 4) were placed in the access cavities of the teeth. After setting of the materials, all specimens were restored with a resin modified glass ionomer. Based on the CIE Lab system, each sample’s total color change (∆E) was obtained before, one, and 90 days after application. Data were statistically analyzed using the Wilcoxon test. Results: According to the results, there was no statistically significant difference in the average tooth discoloration between the groups filled with cold ceramic and in different time periods (P>0.05). While, in the groups filled with MTA Angelus, the difference in the average tooth discoloration in 90 days after application was significantly higher than one day (P<0.05). Conclusion: The results of this study showed that compared to MTA Angelus, cold ceramic causes less tooth discoloration over time and therefore, it can be suggested as a more suitable alternative endodontic cement than MTA Angelus.

Keywords

• mineral trioxide aggregate
• cold ceramic
• tooth discoloration