Effect of Postweld Heat Treatments on Type IV Creep Failure in the Intercritical Heat-Affected Zone of 10% Cr Martensitic Steel Welded with Haynes 282 Filler

Abstract

This study investigated the effect of postweld heat treatment (PWHT) conditions on Type IV failure behavior of 10% Cr martensitic steel welds using Haynes 282 filler. The welded joints were subjected to PWHT at temperatures of 688, 738, and 788 °C for 4 and 8 h. Creep tests were carried out at 600 °C under a stress of 200 MPa. The as-welded joint without PWHT showed Type IV cracking due to growth of voids around Laves phase by localized creep deformation in the intercritical heat-affected zone (ICHAZ). The creep properties of the PWHTed joints at 688 °C were similar to those of the as-welded joints without PWHT. On the other hand, the PWHTed joints at 738 °C exhibited a significantly longer creep life by a lower amount of Laves phase in the ICHAZ than those at 688 °C; this could be a result of the homogenization of ICHAZ microstructure during PWHT at 738 °C. However, the PWHT at 688 and 738 °C showed the same Type IV creep failure mode. Meanwhile, the PWHTed joints at 788 °C exhibited the shortest creep life in this study. The failure location was shifted to the base metal away from the HAZ, and severe plastic deformation occurred due to the softened matrix by excessive tempering.

Keywords

• postweld heat treatment
• heat-affected zone
• creep test
• Type IV cracking
• 10% Cr martensitic steel