Preparation of PEEK-NH2/graphene network structured nanocomposites with high electrical conductivity

Abstract

The percolation thresholds of poly ether ether ketone/graphene (PEEK/Gr) composites in most studies are high due to the random distribution of Gr in the matrix. Here, aminated poly-ether-ether-ketone/graphene network (PEEK-NH2/GN) nanocomposites were prepared by electrostatic adsorption of PEEK-NH2 with positive charges and graphene oxide with negative charges, followed by in -situ reduction and hot-pressing. The GN structure of composites was well presented in the images of scanning electron microscope. The PEEK-NH2/GN nanocomposites exhibited excellent electrical conductivity with a maximum conductivity of 0.0634 S·cm−1 and a percolation threshold as low as 0.25 vol%. In addition, the maximum tensile strength of nanocomposites was reached at 93 MPa when the Gr content was 0.5 wt%. We believe that this approach is a new avenue for the production of low filler high conductive polymer composites with potential commercial prospects in various fields.

Keywords

• aminated poly ether ether ketone
• graphene
• electrostatic adsorption
• conductive network
• electrical property