METAL OXIDE DOPED ANTIBACTERIAL POLYMERIC COATED TEXTILE MATERIALS AND ASSESSEMENT OF ANTIBACTERIAL ACTIVITY WITH ELECTRON SPIN RESONANCE

Abstract

Antibacterial activity of a food conveyor belt is an essential property in some cases. However, every antibacterial chemical is not suitable to contact with food materials. Many metal oxides are suitable option for this purpose. The aim of this study was to investigate antibacterial properties of zinc oxide doped PVC polymer coated with electron spin resonance technique. Therefore, optimum zinc oxide containing PVC paste was prepared and applied to textile surface. Coating construction was designed as double layered, first layer did not contain antibacterial agent, thin second layer contained zinc oxide at 10-35% concentration. Oxygen radicals released from zinc oxide containing polymeric coated surface were spin trapped with DMPO (dimethylpyrroline-N-oxide) spin trap and measured with Electron Spin Resonance (ESR). Besides conveyor belt samples, oxygen radical release from zinc oxide surface was measured with ESR under UV light and dark conditions. Oxygen radical release was determined even at dark conditions. Antibacterial properties were tested with ISO 22196 standard using Listeria innocua species. Measured antibacterial properties were related with ESR results. Higher concentration of zinc oxide resulted in higher antibacterial efficiency. DCFH-DA flourometric assay was carried out to determine oxidative stress insidebacteria. It is tought that, this technique will lead to decrease on the labour and time needed for conventional antibacterial tests.

Keywords

• antibacterial
• conveyor belt
• Electron Spin Resonance
• zinc oxide
• spin trapping