The Effect of Zirconium as an Alloying Additive on the Microstructure and Properties of AlSi9Mg Alloy Cast in Sand Moulds

Abstract

The aim of the study was to select the optimal content of zirconium introduced as an alloying additive to obtain the best strength properties of Al-Si alloy. A technically important disadvantage is the tendency of silumins to form a coarse-grained structure that adversely affects the mechanical properties of castings. To improve the structure, modification processes and alloying additives are used, both of which can effectively refine the structure and thus increase the mechanical properties. According to the Hall-Petch relationship, the finer is the structure, the higher are the mechanical properties of the alloy. The proposed addition of zirconium as an alloying element has a beneficial effect on the structure and properties of silumins, inhibiting the grain growth. The starting material was an aluminium-silicon casting alloy designated as EN AC-AlSi9Mg (AK9). Zirconium (Zr) was added to the alloy in an amount of 0.1%, 0.2%, 0.3%, 0.4% and 0.5% by weight. From the modified alloy, after verification of the chemical composition, samples were cast into sand moulds based on a phenolic resin. The first step in the research was testing the casting properties of alloys with the addition of Zr (castability, density, porosity). In the next step, the effect of zirconium addition on the structure and mechanical properties of castings was determined.

Keywords

• silumins
• precipitation hardening
• alloying additives
• microstructure examinations
• strength tests