Green synthesis, characterization, and photocatalytic activity of superparamagnetic MgFe2O4@ZnAl2O4 nanocomposites

Abstract

Abstract MgFe2O4@ZnAl2O4 magnetic nanocomposites were synthesized with the easy and green sol–gel method, and their photocatalytic efficiency was followed toward degradation of reactive blue 222 (RB222) dye under visible light irradiation. Prepared nanocomposites were fully characterized. The SEM and TEM images revealed the spherical morphology of the produced nanocomposites, with average size of 20–25 nm. The XRD pattern of sample exhibited the successful synthesis of the MgFe2O4@ZnAl2O4 MNCs with crystallite size 13 nm. The saturation magnetization (Ms) of the nanocomposites was examined using VSM, indicating a value of 6.59 emu/g. The absence of Hc and Mr values confirms the superparamagnetic nature of the nanoparticles. In addition, the surface area was calculated to be 78.109 m2/g utilizing BET analysis, and the band gap was determined to be 1.88 eV by DRS analysis. The photocatalytic, photolysis, and adsorption performance were investigated and result shown photodegradation activity was higher than others. These results confirm the synergetic effect between the MgFe2O4@ZnAl2O4 MNCs and visible light irradiation to degradation of organic dye. The results indicate that rapid degradation of 96% of RB222 dye occurred in just 10 min, with a TOC removal rate of approximately 59%. Furthermore, radical scavenger agents also clarified photodegradation of RB222 dye.

Keywords

• Photocatalysis
• Superparamagnetic nanocomposite
• Zinc aluminate
• Sol–gel method
• Reactive blue 222
• Dye degradation