Synthesis of Heterostructure of ZnO@MOF-46(Zn) to Improve the Photocatalytic Performance in Methylene Blue Degradation

Abstract

The heterostructure of ZnO and MOF-46(Zn) was synthesized to improve the photocatalytic performance of ZnO and prove the synergistic theory that presented the coexistence of ZnO and MOF-46(Zn), providing better efficiency than pure ZnO. The heterostructure material was synthesized by using prepared ZnO as a Zn2+ source, which was reacted with 2-aminoterephthalic acid (2-ATP) as a ligand to cover the surface of ZnO with MOF-46(Zn). The ZnO reactant materials were modified by pyrolysis of various morphologies of IRMOF-3 (Zn-MOF) prepared by using CTAB as a morphology controller. The octahedral ZnO obtained at 150 mg of CTAB shows better efficiency for photodegradation, with 85.79% within 3 h and a band gap energy of 3.11 eV. It acts as a starting material for synthesis of ZnO@MOF-46(Zn). The ZnO/MOF-46(Zn) composite was further used as a photocatalyst material in the dye (methylene blue: MB) degradation process, and the performance was compared with that of pure prepared ZnO. The results show that the photocatalytic efficiency with 61.20% in the MB degradation of the heterostructure is higher than that of pure ZnO within 60 min (90.09% within 180 min). The reason for this result may be that the coexistence of ZnO and MOF-46(Zn) can absorb a larger range of energy and reduce the possibility of the electron–hole recombination process.

Keywords

• zinc oxide
• metal-organic framework
• photocatalytic performance
• heterostructure