Simulación y experimentación de laminación plana de placas de aluminio 6063

Abstract

An experimental methodology was generated for understanding the theoretical and practical concepts inherent to cold flat rolling. Aluminium slabs about 100 mm length, 9 mm thickness with different widths: 10 and 30 mm were rolled. A constant 0.3 mm thickness reduction step was performed in order to achieve a thickness reduction greater than 80 %. In the Abaqus® commercial software, a mathematical model was implemented in order to obtain a greater understanding concerning how the process variables affect the fields of stresses and strains that are not observed experimentally. It was found, by mathematical simulation, that a superficial hardening in the plates was produced and the deformation obtained is heterogeneous, which is corroborated physically. Keywords: Flat rolling; 6063 Aluminium; Data acquisition system; Simulation Se generó una metodología experimental para el entendimiento teórico-práctico de los conceptos del proceso de laminación plana en frío. Se laminaron placas de aluminio de aproximadamente 100 mm de longitud y 9 mm de espesor, a diferentes anchos: 10 y 30 mm. Se seleccionó una razón de reducción constante de 0.3 mm para cada paso de laminación, hasta lograr una reducción superior al 80 % en espesor. Se implementó un modelo matemático en el paquete comercial Abaqus® con el fin de obtener un mayor entendimiento sobre la influencia de las variables del proceso (fuerza aplicada y dimensiones de las probetas) en los campos de esfuerzos y deformaciones que, experimentalmente, no se pueden observar. Se encontró, mediante la simulación matemática, que se produce un endurecimiento superficial en las placas y que la deformación obtenida es heterogénea, lo cual se corrobora físicamente.</span

Keywords

• Laminación plana
• Aluminio 6063-Al
• Sistema de adquisición de datos
• Simulación