Abstract

This study investigates the properties of various adhesives and assesses the effects of the coating and drying conditions of aluminum surface treatment agents on adhesion strength and chemical resistance. The adhesion between aluminum and the polymer film is improved through the application of a surface treatment agent to the aluminum surface. This study examines the initial adhesive strength of a manufactured pouch film with respect to the drying temperature and time and evaluates its adhesive strength in the presence of moisture. The results indicate that the residual moisture on the aluminum surface weakens the adhesive strength and significantly affects electrolyte resistance. A noticeable reduction in strength was observed after water spraying, when the drying temperature and time were relatively low during the initial strength measurement. Among the adhesives used for aluminum and CPP lamination, olefin adhesives exhibit less susceptibility to electrolyte effects and have higher adhesive strengths compared to urethane and ester adhesives. Leveraging these characteristics, flexible pouch cells were manufactured and their stability was evaluated. The results confirm that the flexible cells demonstrate excellent stability, exhibiting potential for application in wearable devices.

Keywords

• electric vehicle
• secondary battery
• pouch film
• R2R coating and lamination
• manufacturing process
• flexible battery