Molecules (Jul 2024)

Ferroelectric and Relaxor-Ferroelectric Phases Coexisting Boosts Energy Storage Performance in (Bi<sub>0.5</sub>Na<sub>0.5</sub>)TiO<sub>3</sub>-Based Ceramics

  • Yunting Li,
  • Guangrui Lu,
  • Yan Zhao,
  • Rui Zhao,
  • Jiaqi Zhao,
  • Jigong Hao,
  • Wangfeng Bai,
  • Peng Li,
  • Wei Li

DOI
https://doi.org/10.3390/molecules29133187
Journal volume & issue
Vol. 29, no. 13
p. 3187

Abstract

Read online

With the intensification of the energy crisis, it is urgent to vigorously develop new environment-friendly energy storage materials. In this work, coexisting ferroelectric and relaxor-ferroelectric phases at a nanoscale were constructed in Sr(Zn1/3Nb2/3)O3 (SZN)-modified (Bi0.5Na0.5)0.94Ba0.06TiO3 (BNBT) ceramics, simultaneously contributing to large polarization and breakdown electric field and giving rise to a superior energy storage performance. Herein, a high recoverable energy density (Wrec) of 5.0 J/cm3 with a conversion efficiency of 82% at 370 kV/cm, a practical discharged energy density (Wd) of 1.74 J/cm3 at 230 kV/cm, a large power density (PD) of 157.84 MW/cm3, and an ultrafast discharge speed (t0.9) of 40 ns were achieved in the 0.85BNBT-0.15SZN ceramics characterized by the coexistence of a rhombohedral-tetragonal phase (ferroelectric state) and a pseudo-cubic phase (relaxor-ferroelectric state). Furthermore, the 0.85BNBT-0.15SZN ceramics also exhibited excellent temperature stability (25–120 °C) and cycling stability (104 cycles) of their energy storage properties. These results demonstrate the great application potential of 0.85BNBT-0.15SZN ceramics in capacitive pulse energy storage devices.

Keywords