The effect of Er, Cr:YSGG laser debonding on the bond strength of two ceramic materials to dentin

Abstract

Abstract Objectives Evaluating the bond strength of two ceramic materials to dentin after Er,Cr:YSGG laser debonding. Would laser debonding affect the bond strength of ceramic to dentin? Materials and methods Recently extracted human molars were ground to expose dentin. Forty square shaped samples were prepared from CAD/CAM ceramic blocks. Samples were divided into two groups according to the type of ceramic material; group E: Lithium disilicate and group T: Ultra-translucent Zirconia (n = 20) Each group was divided into two subgroups (n = 10) according to the laser debonding effect (subgroup B: bonded samples, subgroup R: re-bonded samples after laser debonding). Ceramic samples were bonded to dentin using dual cure self-adhesive resin cement. Laser debonding of ceramic samples of subgroups R using Er, Cr:YSGG laser, were then re-bonded again to dentin surface with same resin cement. The Shear bond strength test using Universal testing machine was done. The failure mode was analyzed. Two-way analysis of variance was used to compare the mean bond strength and re-bond strength of two materials. The significance level was set at P ≤ 0.05. Results Two-Way ANOVA showed that ceramic type had a significant effect on the re-bond strength to dentin. The predominant failure mode was adhesive. Conclusions Laser debonding of Lithium disilicate and Ultra translucent Zirconia decreased the re-bond strength to dentin. Deterioration in re-bond strength for Lithium disilicate ceramics was more pronounced than for Ultra translucent Zirconia. Clinical Relevance Deterioration in the bond strength between ceramics & dentin after laser debonding still needs improvement to allow its clinical use.

Keywords

• Laser debonding
• Resin cement
• Shear bond strength
• Er,Cr:YSGG laser
• Ceramics