Effect of Grit Blasting and Polishing Pretreatments on the Microhardness, Adhesion and Corrosion Properties of Electrodeposited Ni-W/SiC Nanocomposite Coatings on 45 Steel Substrate

Abstract

In this study, a grit-blasting pretreatment was used to improve the adhesion, corrosion resistance and microhardness of Ni-W/SiC nanocomposite coatings fabricated using the conventional electrodeposition technique. Prior to deposition, grit blasting and polishing (more commonly used) pretreatments were used to prepare the surface of the substrate and the 3D morphology of the pretreated substrates was characterized using laser scanning confocal microscopy. The coating surface and the cross-section morphology were analyzed using scanning electron microscopy (SEM). The chemical composition, crystalline structure, microhardness, adhesion and corrosion behavior of the deposited coatings were characterized using energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), a microhardness tester, a scratch tester and an electrochemical workstation, respectively. The results indicated that the grit blasting and SiC addition improved the microhardness, adhesion and corrosion resistance. The Ni-W/SiC nanocomposites pretreated by grit blasting exhibited the best adhesion strength, up to 36.5 ± 0.75 N. Its hardness was the highest and increased up to 673 ± 5.47 Hv and its corrosion resistance was the highest compared to the one pretreated by polishing.

Keywords

• nano-composite
• blasting
• pretreatment
• adhesion
• microhardness
• corrosion resistance