The role of Ta on twinnability in nanocrystalline Cu–Ta alloys

Abstract

Nanostructured Cu–Ta alloys show promise as high-strength materials in part due to their limited grain growth. In the present study, we elucidate the role of Ta on the transition from deformation twinning to dislocation-mediated slip mechanisms in nanocrystalline Cu through atomistic simulations and transmission electron microscopy characterization. In particular, computed generalized stacking fault energy curves show that as Ta content increases there is a shift from twinning to slip-dominated deformation mechanisms. Furthermore, heterogeneous twinnability from microstructural defects decreases with an increase in Ta. The computed effect of Ta on plasticity is consistent with the HRTEM observations.

Keywords

• Nanocrystalline
• twinning
• dislocation
• TEM