Ceramic Conversion Treatment of Commercial Pure Titanium with a Pre-Deposited Vanadium Layer

Abstract

Titanium is characterized by poor wear resistance which restricts its application. Ceramic conversion treatment (CCT) is used to modify the surface; however, it is a time-consuming process. In this work, a thin vanadium layer was pre-deposited on the commercial pure titanium (CPTi) samples’ surface, and it increased the oxygen absorption significantly and assisted in obtaining a much thicker oxide layer than those samples without a V layer at the treatment temperatures of 620 °C and 660 °C. The oxidation of the samples pre-deposited with the V layer had a much higher oxidation rate, and V was evenly distributed in the oxide layer. After CCT, all samples had a low wear volume and stable coefficient of friction in comparison to the untreated CPTi sample. A slightly higher wear area in the wear track was observed on the V pre-deposited samples than those samples without vanadium, especially those with a thicker oxide layer (>4 µm). This might be associated with defects in a thicker oxide layer and insufficient support from a shallower oxygen diffusion zone or hard debris created at the initial stage. Vanadium in the oxide layer reduced the contact angles of the surface and increased the wettability significantly.

Keywords

• titanium
• vanadium
• oxidation
• ceramic conversion treatment