Chitosan Capped Copper Oxide Nanocomposite: Efficient, Recyclable, Heterogeneous Base Catalyst for Synthesis of Nitroolefins

Abstract

In this article, chitosan copper oxide nanocomposite was synthesized by the solution casting method under microwave irradiation. The nanocomposite solution was microwave irradiated at 300 watt for 3 min under optimal irradiation conditions. By suppressing particle agglomeration, the chitosan matrix was successfully used as a metal oxide stabilizer. The goal of this research was to create, characterize, and test the catalytic potency of these hybrid nanocomposites in a number of well-known organic processes. The prepared CS-CuO nanocomposites were analyzed by different techniques, including Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and field emission scanning electron microscopy (FESEM). Moreover, energy-dispersive X-ray spectroscopy (EDS) was used to measure the copper content in the prepared nanocomposite film. The finger-print peaks in the FTIR spectrum at around 632–502 cm−1 confirmed the existence of the CuO phase. The CS-CuO nanocomposite has been shown to be an efficient base promoter for nitroolefin synthesis via the nitroaldol reaction (Henry reaction) in high yields. The reaction variables were studied to improve the catalytic approach. Higher reaction yields, shorter reaction times, and milder reaction conditions are all advantages of the technique, as is the catalyst’s reusability for several uses.

Keywords

• chitosan
• copper oxide nanoparticles
• heterogeneous catalysis
• Nitroolefins