Deposition of a SiO₂ Shell of Variable Thickness and Chemical Composition to Carbonyl Iron: Synthesis and Microwave Measurements

Abstract

Protective SiO2 coating deposited to iron microparticles is highly demanded both for the chemical and magnetic performance of the latter. Hydrolysis of tetraethoxysilane is the crucial method for SiO2 deposition from a solution. The capabilities of this technique have not been thoroughly studied yet. Here, two factors were tested to affect the chemical composition and the thickness of the SiO2 shell. It was found that an increase in the hydrolysis reaction time thickened the SiO2 shell from 100 to 200 nm. Moreover, a decrease in the acidity of the reaction mixture not only thickened the shell but also varied the chemical composition from SiO3.0 to SiO8.6. The thickness and composition of the dielectric layer were studied by scanning electron microscopy and energy-dispersive X-ray analysis. Microwave permeability and permittivity of the SiO2-coated iron particles mixed with a paraffin wax matrix were measured by the coaxial line technique. An increase in thickness of the silica layer decreased the real quasi-static permittivity. The changes observed were shown to agree with the Maxwell Garnett effective medium theory. The new method developed to fine-tune the chemical properties of the protective SiO2 shell may be helpful for new magnetic biosensor designs as it allows for biocompatibility adjustment.

Keywords

• protective coating
• soft magnetic powder
• microwave permittivity
• core–shell particles