Molecules (Jun 2024)

Effects of TiO<sub>2</sub> Nanoparticles Synthesized via Microwave Assistance on Adsorption and Photocatalytic Degradation of Ciprofloxacin

  • Debora Briševac,
  • Ivana Gabelica,
  • Davor Ljubas,
  • Arijeta Bafti,
  • Gordana Matijašić,
  • Lidija Ćurković

DOI
https://doi.org/10.3390/molecules29122935
Journal volume & issue
Vol. 29, no. 12
p. 2935

Abstract

Read online

In this study, the optimal microwave-assisted sol-gel synthesis parameters for achieving TiO2 nanoparticles with the highest specific surface area and photocatalytic activity were determined. Titanium isopropoxide was used as a precursor to prepare the sol (colloidal solution) of TiO2. Isopropanol was used as a solvent; acetylacetone was used as a complexation moderator; and nitric acid was used as a catalyst. Four samples of titanium dioxide were synthesized from the prepared colloidal solution in a microwave reactor at a temperature of 150 °C for 30 min and at a temperature of 200 °C for 10, 20, and 30 min. The phase composition of the TiO2 samples was determined by X-ray diffraction analysis (XRD) and Fourier-transform infrared spectroscopy (FTIR). Nitrogen adsorption/desorption isotherms were used to determine the specific surface area and pore size distributions using the Brunauer–Emmett–Teller (BET) method. The band-gap energy values of the TiO2 samples were determined by diffuse reflectance spectroscopy (DRS). The distribution of Ti and O in the TiO2 samples was determined by SEM-EDS analysis. The effects of adsorption and photocatalytic activity of the prepared TiO2 samples were evaluated by the degradation of ciprofloxacin (CIP) as an emerging organic pollutant (EOP) under UV-A light (365 nm). The results of the photocatalytic activity of the synthesized TiO2 nanoparticles were compared to the benchmark Degussa P25 TiO2. Kinetic parameters of adsorption and photocatalysis were determined and analyzed. It was found that crystalline TiO2 nanoparticles with the highest specific surface area, the lowest energy band gap, and the highest photocatalytic degradation were the samples synthesized at 200 °C for 10 min. The results indicate that CIP degradation by all TiO2 samples prepared at 200 °C show a synergistic effect of adsorption and photocatalytic degradation in the removal process.

Keywords