Study of the Nature of the Destruction of Coatings Based on the ZrN System Deposited on a Titanium Alloy Substrate

Abstract

The fracture strength was compared in a scratch test of coatings based on the ZrN system with the introduction of Ti, Nb and Hf, which were deposited on a titanium alloy substrate. The coatings were deposited using Controlled Accelerated Arc (CAA-PVD) technology. In coatings that simultaneously include Zr and Ti, a nanolayer structure is formed, while in coatings without Ti, the formation of a monolithic single-layer structure is observed. The comparison was carried out according to two parameters: adhesion strength to the substrate and overall coating strength. The (Zr,Hf)N coating showed better resistance to destruction, but had worse adhesion to the substrate. As a result, although the coating is retained directly in the scribing groove, a large area of delamination and destruction is formed around the groove. The (Ti,Zr,Nb)N coating, with its somewhat lower strength, has a high adhesion to the substrate; no noticeable delamination is observed along the groove boundary. In this paper, not only is the fracture resistance of various coatings deposited on a titanium alloy substrate compared, but the nature of this fracture is also investigated depending on the composition of the coatings.

Keywords

• titanium alloy
• coatings
• adhesion
• wear
• scratch test